Polycarbonate build plate…. No bed heat Success!!!
-
i am digging this! maybe paired with a heated chamber to control shrinkage and warping?
-
Yes that is exactly what it needs… I have an enclosed chamber which helps but heated would be ideal
I might be able to get away with adding some radiant heat barrier to the back and side panels ... the windows on the side i can print fan holders for when doing things like PLA
-
tomorrow i have to print off some more of these bearings but then ill try Igus iglidur filament which is another self lubricating difficult to print experiment for this build plate
-
I've read about polycarbonate build plates before and the tenor was, the parts often stick too good. Maybe it's the sanding, that makes all the difference? Would it work with shotblasting too? I guess it depends on the stuff you shoot at it?
Where did you get the POM filament from? ( Why do they offer it, when it is "known" to be unprintable? )
I've made these 2040-sliders from PTFE, but POM would be much better I guess. -
-
yes many filaments stick too well if the surface is shiny sanding prevents that… sandblasting works too just i would use a fine sand.... with Acetal POM i found it does not stick at all if not sanded really well... kind of a reversal to other filaments
-
to answer your question i bought it from Matterhackers but they quit selling it (most likely why) a google search will reveal the difficulties even with people claiming its unprintable. Gizmo Dorks still has it.
-
where did you find ptfe filament?
-
-
Also when parts are stuck really well, flexing the plate in different directions helps pop the part off. usually just a twist will take a decent size part off
-
I bought a couple of 3mm PC sheet (one in white, one in transparent) in a local advertisement makers store here in Spain:
I will test both to see which one works better with the IR Sensor and I will sand them and make some tests… I will let you know how this progress :), I'm really excited about @whitewolf's PC bed, looks really promising.
Cheers!
-
I have been runnning PEI 3mm from the start, prep with a quick sand @ 600 grit then wipe with alcohol. sticks very well and yes some times too good and i have to let the bed cool before i can get the print off but 750 watt heater might have something to do with that too. I havent tried anything but PLA yet, still learning the craft so have not jumped to other filaments yet as i thought it would be easier to learn with something easy like PLA is supposed to be… This shows real promise though so i am curious to say the least.
-
PLA is forgiving but dont be affraid of other filaments. I recommend you try Taulman Guidline and Taulman blueprint products next they are easy to print with and have better properties than PLA or ABS. Personally I dont care for ABS and only use PLA for tinkering and prototype iteration. Honestly I love most of the Taulman line
Matterhackers has some flexibles that make printing with flex easier in their pro line.
I have not actually used it yet but ordered the sample pack of RigidInk PLA+…. many people swear by RigidInk PLA+ as being the gold standard for Tough PLA parts
-
I tried PLA+ but gave up on it. It sticks far too well to plain heated glass and to PEI for me. Possibly I should try again with a lower bed temperature. But if you have problems getting the print to adhere to the bed, it might be just what you need.
-
I tried PLA+ but gave up on it. It sticks far too well to plain heated glass and to PEI for me. Possibly I should try again with a lower bed temperature. But if you have problems getting the print to adhere to the bed, it might be just what you need.
As far as the PC bed goes as noted above people in the past gave up on it due to sticking too well. What gave me the idea to try PC sanded was because of my Fleks3D build plate being made from PC with what appears to be a etched maybe sandblasted surface. Using any type of heat on most filaments results in parts which are near impossible to remove, I think a combination of the sanding and lack of heat is what makes it possible.
So you might try the Pei again with no heat on PLA+ or give PC a try… i'll let you know in a few days how PLA+ works with PC
-
Good idea sanding it, its a cheap readily available material. How well does it work with ABS? Can you print ABS cold onto PC?
-
I have not done ABS, because I use other filaments in place of ABS but in another thread here a user commented that he tried it with ABS and 0 bed heat without issue.
-
PLA is forgiving but dont be affraid of other filaments. I recommend you try Taulman Guidline and Taulman blueprint products next they are easy to print with and have better properties than PLA or ABS. Personally I dont care for ABS and only use PLA for tinkering and prototype iteration. Honestly I love most of the Taulman line
Matterhackers has some flexibles that make printing with flex easier in their pro line.
I have not actually used it yet but ordered the sample pack of RigidInk PLA+…. many people swear by RigidInk PLA+ as being the gold standard for Tough PLA parts
I have some taulman 910 sitting in wait for acceptable print quality so i can reproduce some printer parts and ultimately some replacement parts for my old sailboat. At what point do i need to consider temp upgrade beyond aluminum? Have all metal hot end now with brass tips but am guessing copper heater block& ss tip not to mention heat sensor upgrade so i can print higher temp stuff. I thought PC was 1 of those hi temp materials, right? so guessing you are well beyond those upgrades already…
i am still a newbie but have run a couple rolls of matterhacker PLA filament that worked very well for me. this latest roll of "USA FIL" pla is almost as flexible as ABS and feels rubberized post print which is cool but tore my machine to pieces when i screwed up retract setting and am having to reinvent the wheel to get it dialed in again LOL lots to do this weekend...ugh
-
So I have not printed PC, I am printing on 1/8th inch PC build plate. Yes I have a copper heat block with copper nozzles and PT100 sensor.
The PLA+ from RigidInk is just that rigid and very strong. It actually takes much different slicer settings to standard PLA (to my understanding).
I have Taulman 910 but I recommend using Taulman Guidl!ne for your printer and sailboat parts. It is not sensitive to water absorption like the Nylons are and is stronger than their TechG and close to 910 in strength but a lot easier to print. Blueprint is another one to check out.
-
thank you Sir! i will definitely look into that.
-
Good idea sanding it, its a cheap readily available material. How well does it work with ABS? Can you print ABS cold onto PC?
I tried both ABS and PETG and both worked.
-
I've read about polycarbonate build plates before and the tenor was, the parts often stick too good. Maybe it's the sanding, that makes all the difference? Would it work with shotblasting too? I guess it depends on the stuff you shoot at it?
Where did you get the POM filament from? ( Why do they offer it, when it is "known" to be unprintable? )
I've made these 2040-sliders from PTFE, but POM would be much better I guess.Where did you find PTFE filament? I have searched and only see a press announcement of 3M's patent pending filament.
-
So just to update everyone, I am in the early testing phase of Igus iglidur filament. First I tried with the settings used for the Acetal POM, I did use 55c bed heat with Acetal because combined with a small brim, it completely eliminated warping. For Igus Iglidur though it cause some serious bed adhesion so I am retrying now with no bed heat.
One of the things that I found interesting is starting with the acetal pom temp of 220 which is the low end of iglidur, I did not get any layer adhesion and was able to seperate each layer. Inspecting it was interesting because at that temp it has a rough paper feel to it.
-
I was lazy and didnt remove the brim from the slicer settings but Igus Iglidur does not need it. It sticks perfectly to the PC with no bed heat and no warping.
I do have an enclosed printer which is recommended for this filament. Others have had success just covering their printer with painters plastic.
I will compare the Acetal Pom and Iglidur in another thread soon as i do not want to derail the thread subject but 255c was the magic temp for the hotend.
Matter hackers temps are wrong manufacturer website says 250c to 260c